20 Litre Nitobond, Brand Fosroc, Form Liquid

Uses for making of polymer modifi ed mortar and screeds, Repair slurry coat, Bonding agent, Of worn as base, Damaged and spalled concrete for waterproofing. Advantages simple for application gauged as, Single component required. Provides superior attachment to concrete, Adhesion plaster, Masonry, Etc. Provides, Stone work mortar with improved durability impermeability to chlorides as well as other detrimental substances agents. Provides waterproof and plasters and, Cohesive screeds impermeable slurry coat. Improves tensile and fl exural properties of cement thereby reduces cracking. Compatible with all common hydraulic cements. Cost eff ective and economical description nitobond sbr 300 is modifi ed styrene butadiene emulsion purpose-built for implement as a bonding aid and gauging liquid for cementitious systems. It is resistant to hydrolysis and can therefore is applicable to external applications too. Technical support fosroc provides a technical advisory service supported by a dedicated group of specialists in the field. Chemical resistance cementitious based materials have limited chemical resitance. The introduction of nitobond sbr 300 to cement mortars reduces permeability and therefore helps reduce the pace of attack by aggressive chemicals. Laitence must be taken away by mechanical means. Smooth substrates must be mechanically roughened e. G. Needle gun, By scabbling or grit blasting to provide an adequate key. Corroded reinforcing steel should be exposed around its full circumference and Purified to eliminate all loose deposits and deterioration deposits. You will find it to be always preferably to clean the steel for a luminous condition. Use of emery cloth, Grit or sand blasting is recommended. Surface preparation the object of the outer layer preparation is to realize a clean sound surface with a good mechanical key. All substrates should be cleaned and free of dust, Paint, Grease, Corrosion, Oil, Plaster deposits, And any other deleterious substances. Priming reinforcing steel must be primed with nitozinc primer immediately after cleaning. The concrete substrate ought to be fully dampened alongside water and any excess water removed before being primed by thoroughly scrubbing in a slurry coat of1 volume nitbond sbr latex to 1 volume water to 3 volumes fresh cement. To achieve obtain a smooth consistency the cement should be blended slowly into the liquids. Stir frequently during use to off set settlement. Avoid puddling of the slurry coat. The topping must can be used on to the wet slurry. If the slurry dries out it must be removed and the clean substrate reprimed. Additional guidance prepare surfaces thoroughly. Toe, In at edges wherever possible to avoid feather edging. All surfaces including edges must be primed. All applications should be wet the primer, On wet must not have the opportunity to dry. The extent of added water in the mix designs may need adjustment to achieve the required consistency. In general water content must be maintained to the minimum necessary. For consistent performance the implementation of clean, Dry sand is recommended. Where wet sand is utilized for, Reduce the addition of water as appropriate. In order to prevent mortars should, Rapid drying be properly cured with curing compound, Concure wb. Protect uncured mortar from frost. Do not retemper mortar or primer after initial set. Lowest permissible application temperature is 100c. For permanently immersed conditions consult local fosroc office.